IS400

La solution pour circuits rigides et multicouches à Tg standard

Plus de détails

IS400

Ajouter au panier

Présentation du produit à venir.

    Caracteristiques Valeur typique [Specifications] (Certification)
    Glass Transition (Tg) by DSC 150°C [110-150] (IPC-TM-650 2.4.25)
    Decomposition (Td) by TGA @ 5% weight loss 330°C (ASTM D3850)
    T260 over 60 Minutes (IPC-TM-650 2.4.25)
    T288 over 10 Minutes (IPC-TM-650 2.4.25)
    CTE, Z-axis, Pre-Tg 50 ppm/°C [AABUS] (IPC-TM-650 2.4.24)
    CTE, Z-axis, Post-Tg 250 ppm/°C [AABUS] (IPC-TM-650 2.4.24)
    CTE, X-, Y-axes, Pre-Tg 13 ppm/°C [AABUS] (IPC-TM-650 2.4.24)
    CTE, X-, Y-axes, Post-Tg 14 ppm/°C (IPC-TM-650 2.4.24)
    Z-axis Expansion (50-260°C) 3.30% [AABUS] (IPC-TM-650 2.4.24)
    Thermal Conductivity 0.36 W/mK (ASTM D5930)
    Thermal Stress 10 sec @ 288°C (550.4°F) Unetched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
    Thermal Stress 10 sec @ 288°C (550.4°F) Etched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
    Volume Resistivity 96/35/90 4.0x10exp8 [1.0x10exp4 MOhms-cm] (IPC-TM-650 2.5.17.1)
    Volume Resistivity At elevated temperature 7.0x10exp7 MOhms-cm [1.0x10exp3 MOhms-cm] (IPC-TM-650 2.5.17.1)
    Surface Resistivity 96/35/90 3.0x10exp6 [1.0x10exp4 MOhms] (IPC-TM-650 2.5.17.1)
    Surface resistivity At elevated temperature 5.4x10exp6 MOhms [1.0x10exp3 MOhms] (IPC-TM-650 2.5.17.1)
    Dielectric Breakdown over 50 kV (IPC-TM-650 2.5.6)
    Arc Resistance 120 Seconds [60] (IPC-TM-650 2.5.1)
    Electric Strength 48 kV/mm 1100V/mil [29 kV/mm 736V/mil] (IPC-TM-650 2.5.6.2)
    Comparative Tracking Index (CTI) 3 Class Volts [175-249] (UL-746A ASTM D3638)
    Peel Strength Low profile cooper foil and very low profile - All copper weights over 17 microns 1.05N/mm 8.0lb/inch [0.70N/mm 4.0lb/inch] (IPC-TM-650 2.4.8)
    Peel Strength Standard profile cooper After thermal stress 1.45N/mm 9.0lb/inch [1.05N/mm 6.0lb/inch] (IPC-TM-650 2.4.8.3)
    Peel Strength Standard profile cooper At 125 °C 1.25N/mm 8.0lb/inch [0.70N/mm 4.0lb/inch]
    Peel Strength Standard profile cooper After process solutions 1.45N/mm 9.0lb/inch [0.80N/mm 4.5lb/inch]
    Flexural Strength Lengthwise direction 82 000 lb/inch² (IPC-TM-650 2.4.4)
    Flexural Strength Crosswise direction 66 600 lb/inch² (IPC-TM-650 2.4.4)
    Tensile Strength Lengthwise direction 51 213 lb/inch²
    Tensile Strength Crosswise direction 41 675 lb/inch²
    Moisture Absorption 0.18% [0.8] (IPC-TM-650 2.6.2.1)
    Flammability (Laminate & prepreg as laminated) V-0 Rating [V-0] (UL94)
    Max Operating Temperature 130°C
    Young's Modulus Grain direction 3663ksi (ww)
    Young's Modulus Fill direction 3328ksi (ww)
    Poisson's Ratio Grain direction 0.183 (xx)
    Poisson's Ratio Fill direction 0.151 (xx)
    Dk, Permittivity Tested at 50% resin @ 500MHz 3.90 (IPC-TM-650 2.5.5.9)
    Df, Loss Tangent Tested at 50% resin @ 500 MHz 0.022 (IPC-TM-650 2.5.5.9)
    Dk, Permittivity Tested at 50% resin @ 1MHz 4.00 [5.40] (IPC-TM-650 2.5.5.3)
    Df, Loss Tangent Tested at 50% resin @ 1 MHz 0.020 [0.035] (IPC-TM-650 2.5.5.3)

    Les informations ci-dessus ainsi que les fiches techniques sont fournies a titre indicatif. Seuls les documents remis le jour de la vente peuvent servir de reference.

Contactez-nous

Notre service client est disponible du lundi au vendredi de 9H à 18H

Tél. :+33 (0)6 31 29 78 00

Contacter notre service client
Powered by Algolys & TechInformatique Web Agency