Epoxy Standards

DE104

La référence pour circuits rigides SF et DF

En savoir plus

Présentation du produit à venir.

Fiche technique
Caracteristiques Valeur typique [Specifications] (Certification)
Glass Transition (Tg) by DSC 135°C (IPC-TM-650 2.4.25)
Decomposition (Td) by TGA @ 5% weight loss 315°C (ASTM D3850)
T260 12 Minutes (IPC-TM-650 2.4.24.1)
T288 (IPC-TM-650 2.4.25)
CTE, Z-axis, Pre-Tg 70ppm/°C (IPC-TM-650 2.4.24)
CTE, Z-axis, Post-Tg 250ppm/°C (IPC-TM-650 2.4.24)
CTE, X-, Y-axes, Pre-Tg 16/13ppm/°C (IPC-TM-650 2.4.24)
CTE, X-, Y-axes, Post-Tg 14/7ppm/°C (IPC-TM-650 2.4.24)
Z-axis Expansion (50-260°C) 3.0% (IPC-TM-650 2.4.24)
Thermal Conductivity 0.36 W/mK (ASTM D5930)
Thermal Stress 10 sec @ 288°C (550.4°F) Unetched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
Thermal Stress 10 sec @ 288°C (550.4°F) Etched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
Dk, Permittivity Tested at 50% resin @ 100MHz 4.46 [Split Post Method]
Dk, Permittivity Tested at 50% resin @ 1GHz 4.37 [Split Post Method] (IPC-TM-650 2.5.5.9)
Dk, Permittivity Tested at 50% resin @ 2GHz 4.35 [Split Post Method] (IPC-TM-650 2.5.5.5)
Dk, Permittivity Tested at 50% resin @ 5GHz 4.32 [Split Post Method]
Df, Loss Tangent Tested at 50% resin @ 100 MHz 0.020 [Split Post Method]
Df, Loss Tangent Tested at 50% resin @ 1 GHz 0.022 [Split Post Method]
Df, Loss Tangent Tested at 50% resin @ 2 GHz 0.023 [Split Post Method] (IPC-TM-650 2.5.5.9)
Df, Loss Tangent Tested at 50% resin @ 5 GHz 0.024 [Split Post Method] (IPC-TM-650 2.5.5.5)
Volume Resistivity 96/35/90 (IPC-TM-650 2.5.17.1)
Volume Resistivity After moisture resistance 1.3x10exp6MOhms-cm [1.0x10exp4] (IPC-TM-650 2.5.17.1)
Volume Resistivity At elevated temperature 3.4x10exp7MOhms-cm [1.0x10exp3] (IPC-TM-650 2.5.17.1)
Surface Resistivity 96/35/90 (IPC-TM-650 2.5.17.1)
Surface Resistivity After moisture resistance 1.0x10exp6MOhms [1.0x10exp4] (IPC-TM-650 2.5.17.1)
Surface resistivity At elevated temperature 7.2x10exp6MOhms [1.0x10exp3] (IPC-TM-650 2.5.17.1)
Dielectric Breakdown over 50 kV [40] (IPC-TM-650 2.5.6)
Arc Resistance 105 Seconds [60] (IPC-TM-650 2.5.1)
Electric Strength 54kV/mm 1350V/mil [29kV/mm 736V/mil] (IPC-TM-650 2.5.6.2)
Comparative Tracking Index (CTI) 2 Class Volts
Peel Strength Low profile cooper foil and very low profile - All copper weights over 17 microns 1.23N/mm 7.0lb/inch [0.70N/mm 4.0lb/inch] (IPC-TM-650 2.4.8)
Peel Strength Standard profile cooper After thermal stress 1.58N/mm 9.0lb/inch [1.05N/mm 6.0lb/inch] (IPC-TM-650 2.4.8.3)
Peel Strength Standard profile cooper At 125 °C 1.23N/mm 7.0lb/inch [0.70N/mm 4.0lb/inch]
Peel Strength Standard profile cooper After process solutions 1.58N/mm 9.0lb/inch [0.80N/mm 4.5lb/inch] (IPC-TM-650 2.4.8)
Flexural Strength Lengthwise direction 84 000 lb/inch² (IPC-TM-650 2.4.4)
Flexural Strength Crosswise direction 65 200 lb/inch² (IPC-TM-650 2.4.4)
Tensile Strength Lengthwise direction 57 000 lb/inch²
Tensile Strength Crosswise direction 42 400 lb/inch²
Moisture Absorption 0.3% [0.8] (IPC-TM-650 2.6.2.1)
Flammability (Laminate & prepreg as laminated) V-0 Rating [V-0] (UL94)
Max Operating Temperature 130°C [UL Cert]
Dk, Permittivity Tested at 50% resin @ 500MHz 4.40 [5.40] (IPC-TM-650 2.5.5.3)
Df, Loss Tangent Tested at 50% resin @ 500 MHz 0.021 [0.035] (IPC-TM-650 2.5.5.3)

 

Les informations ci-dessus ainsi que les fiches techniques sont fournies a titre indicatif. Seuls les documents remis le jour de la vente peuvent servir de reference.

Télécharger

DE104 - Data sheet
Fiche technique du DE104 (US)

FR402

Gamme circuits rigides SF et DF

En savoir plus

Présentation du produit à venir.

Fiche technique
Caracteristiques Valeur typique [Specifications] (Certification)
Glass Transition (Tg) by DSC 140°C [170-200] (IPC-TM-650 2.4.25)
Decomposition (Td) by TGA @ 5% weight loss 320°C [170-200] (ASTM D3850)
T260 30 Minutes (IPC-TM-650 2.4.25)
T288 over 5 Minutes (IPC-TM-650 2.4.25)
CTE, Z-axis, Pre-Tg 50ppm/°C [AABUS] (IPC-TM-650 2.4.24)
CTE, Z-axis, Post-Tg 250ppm/°C (IPC-TM-650 2.4.24)
CTE, X-, Y-axes, Pre-Tg 15ppm/°C [AABUS] (IPC-TM-650 2.4.24)
CTE, X-, Y-axes, Post-Tg 17ppm/°C (IPC-TM-650 2.4.24)
Z-axis Expansion (50-260°C) 4.2% (IPC-TM-650 2.4.24)
Thermal Conductivity 0.36W/mK (ASTM D5930)
Thermal Stress 10 sec @ 288°C (550.4°F) Unetched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
Thermal Stress 10 sec @ 288°C (550.4°F) Etched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
Dk, Permittivity Tested at 50% resin @ 1GHz 4.25 [5.4] (IPC-TM-650 2.5.5.5)
Df, Loss Tangent Tested at 50% resin @ 1 GHz 0.015 [0.035] (IPC-TM-650 2.5.5.5)
Volume Resistivity 96/35/90 4.0x10exp8 MOhms-cm [1.0x10exp4] (IPC-TM-650 2.5.17.1)
Volume Resistivity At elevated temperature 7.0x10exp7 MOhms-cm [1.0x10exp3] (IPC-TM-650 2.5.17.1)
Surface Resistivity 96/35/90 3.0x10exp6 MOhms [1.0x10exp4] (IPC-TM-650 2.5.17.1)
Surface resistivity At elevated temperature 6.0x10exp6 MOhms [1.0x10exp6] (IPC-TM-650 2.5.17.1)
Dielectric Breakdown over 50kV (IPC-TM-650 2.5.6)
Arc Resistance 120 Seconds [60] (IPC-TM-650 2.5.1)
Electric Strength 29kV/mm 1100V/mil [48kV/mm 736V/mil] (IPC-TM-650 2.5.6.2)
Comparative Tracking Index (CTI) 3Class 175-249Volts (UL-746A ASTMD3638)
Peel Strength Low profile cooper foil and very low profile - All copper weights over 17 microns 1.05N/mm 8.0lb/inch [0.70N/mm 4.0lb/inch] (IPC-TM-650 2.4.8)
Peel Strength Standard profile cooper After thermal stress 1.45N/mm 9.0lb/inch [1.05N/mm 6.0lb/inch] (IPC-TM-650 2.4.8.3)
Peel Strength Standard profile cooper At 125 °C 1.25N/mm 8.0lb/inch [0.70N/mm 4.0lb/inch]
Peel Strength Standard profile cooper After process solutions 1.45N/mm 9.0lb/inch [0.80N/mm 4.5lb/inch]
Flexural Strength Lengthwise direction 100,300 lb/inch² (IPC-TM-650 2.4.4)
Flexural Strength Crosswise direction 67,300 lb/inch² (IPC-TM-650 2.4.4)
Tensile Strength Lengthwise direction 60,000 lb/inch²
Tensile Strength Crosswise direction 43,150 lb/inch²
Moisture Absorption 0.3% [0.8] (IPC-TM-650 2.6.2.1)
Flammability (Laminate & prepreg as laminated) V-0 Rating [V-0] (UL 94)
Max Operating Temperature 130°C [UL Cert]
Dk, Permittivity Tested at 50% resin @ 500MHz 4.27 [5.4] (IPC-TM-650 2.5.5.9)
Df, Loss Tangent Tested at 50% resin @ 500 MHz 0.015 [0.035] (IPC-TM-650 2.5.5.9)
Dk, Permittivity Tested at 50% resin @ 1MHz 4.60 [5.4] (IPC-TM-650 2.5.5.3)
Df, Loss Tangent Tested at 50% resin @ 1 MHz 0.016 [0.035] (IPC-TM-650 2.5.5.3)FR402 - Data sheet
Fiche technique du FR402 (US)

 

Les informations ci-dessus ainsi que les fiches techniques sont fournies a titre indicatif. Seuls les documents remis le jour de la vente peuvent servir de reference.

Télécharger

FR402 - Data sheet
Fiche technique du FR402 (US)

FR406

Le matériau standard pour multicouches

En savoir plus

Présentation du produit à venir.

Fiche technique
Caracteristiques Valeur typique [Specifications] (Certification)
Glass Transition (Tg) by DSC 170°C [170-200] (IPC-TM-650 2.4.25)
Decomposition (Td) by TGA @ 5% weight loss 300°C (ASTM D3850)
T260 10 Minutes (IPC-TM-650 2.4.25)
T288 over 2 Minutes (IPC-TM-650 2.4.25)
CTE, Z-axis, Pre-Tg 60ppm/°C [AABUS] (IPC-TM-650 2.4.24)
CTE, Z-axis, Post-Tg 250ppm/°C (IPC-TM-650 2.4.24)
CTE, X-, Y-axes, Pre-Tg 13ppm/°C [AABUS] (IPC-TM-650 2.4.24)
CTE, X-, Y-axes, Post-Tg 14ppm/°C (IPC-TM-650 2.4.24)
Z-axis Expansion (50-260°C) 3.5% (IPC-TM-650 2.4.24)
Thermal Conductivity 0.3-0.4W/mK (ASTM D5930)
Thermal Stress 10 sec @ 288°C (550.4°F) Unetched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
Thermal Stress 10 sec @ 288°C (550.4°F) Etched Pass Rating [Pass Visual] (IPC-TM-650 2.4.13.1)
Dk, Permittivity Tested at 50% resin @ 100MHz 4.00 [5.4] (IPC-TM-650 2.5.5.3)
Dk, Permittivity Tested at 50% resin @ 1GHz 3.95 (IPC-TM-650 2.5.5.9)
Dk, Permittivity Tested at 50% resin @ 2GHz 3.93 (IPC-TM-650 2.5.5.5)
Dk, Permittivity Tested at 50% resin @ 5GHz 3.92 (IPC-TM-650 2.5.5.5)
Dk, Permittivity Tested at 50% resin @ 10GHz 3.92 (IPC-TM-650 2.5.5.5)
Df, Loss Tangent Tested at 50% resin @ 100 MHz 0.0130 [0.035] (IPC-TM-650 2.5.5.3)
Df, Loss Tangent Tested at 50% resin @ 1 GHz 0.0161 (IPC-TM-650 2.5.5.9)
Df, Loss Tangent Tested at 50% resin @ 2 GHz 0.0167 (IPC-TM-650 2.5.5.5)
Df, Loss Tangent Tested at 50% resin @ 5 GHz 0.0172 (IPC-TM-650 2.5.5.5)
Volume Resistivity 96/35/90 9.0x10exp7 MOhms-cm [1.0x10exp6] (IPC-TM-650 2.5.17.1)
Volume Resistivity At elevated temperature 3.0x10exp7 MOhms-cm [1.0x10exp3] (IPC-TM-650 2.5.17.1)
Surface Resistivity 96/35/90 3.0x10exp8 MOhms [1.0x10exp4] (IPC-TM-650 2.5.17.1)
Surface resistivity At elevated temperature 8.0x10exp8 MOhms [1.0x10exp3] (IPC-TM-650 2.5.17.1)
Dielectric Breakdown over 50kV [40] (IPC-TM-650 2.5.6)
Arc Resistance 90 Seconds [60] (IPC-TM-650 2.5.1)
Electric Strength 44kV/mm 1100V/mil [30kV/mm 750V/mil] (IPC-TM-650 2.5.6.2)
Comparative Tracking Index (CTI) 3Class 175-249Volts (UL-746A ASTMD3638)
Peel Strength Low profile cooper foil and very low profile - All copper weights over 17 microns 1.19N/mm 7.0lb/inch [0.70N/mm 4.0lb/inch] (IPC-TM-650 2.4.8)
Peel Strength Standard profile cooper After thermal stress 1.19N/mm 7.0lb/inch [0.80N/mm 4.5lb/inch] (IPC-TM-650 2.4.8.3)
Peel Strength Standard profile cooper At 125 °C 1.19N/mm 7.0lb/inch [0.70N/mm 4.0lb/inch]
Peel Strength Standard profile cooper After process solutions 1.60N/mm 9.0lb/inch [0.55N/mm 3.0lb/inch]
Flexural Strength Lengthwise direction 93,700 lb/inch² (IPC-TM-650 2.4.4)
Flexural Strength Crosswise direction 78,200 lb/inch² (IPC-TM-650 2.4.4)
Tensile Strength Lengthwise direction 62,950 lb/inch²
Tensile Strength Crosswise direction 47,680 lb/inch²
Moisture Absorption 0.2% (IPC-TM-650 2.6.2.1)
Flammability (Laminate & prepreg as laminated) V-0 Rating [V-0] (UL 94)
Max Operating Temperature 130°C [UL Cert]
Young's Modulus Grain direction 3684ksi(ww)
Young's Modulus Fill direction 3116ksi (ww)
Poisson's Ratio Grain direction 0.191 (xx)
Poisson's Ratio Fill direction 0.154 (xx)
Peel Strength Standard profile cooper 1.60N/mm 9.0lb/inch (IPC-TM-650 2.4.8.2)
Df, Loss Tangent Tested at 50% resin @ 10 GHz 0.0172 (IPC-TM-650 2.5.5.5)

 

Les informations ci-dessus ainsi que les fiches techniques sont fournies a titre indicatif. Seuls les documents remis le jour de la vente peuvent servir de reference.

Télécharger

FR406 - Data sheet
Fiche technique du FR406 (US)